AerMet ® 100 (AMS 6532)

 Technical Data Sheet

AerMet® 100 (UNS K92580) is a alloy that has been designed to have properties of excellent hardness and strength combined with exceptional ductility and toughness. AM 100 is used in applications that require high fracture toughness and excellent resistance to stress corrosion cracking and fatigue. AerMet® 100 is considered as a candidate for use in applications such as Armor, Fasteners, Landing Gear, Jet Engine Shafts, Structural Members, Drive Shafts, Structural Tubing. Aermet 100 bar is supplied in the normalized and overaged condition (maximum hardness 372HB) ready for subsequent heat treatment.

Heat Treatment: Aermet 100 bar (to AMS 6532) is supplied in the normalized and overaged as follows:
Normalize: 1650 °F ± 25 (899 °C ± 14) for 60 minutes ± 15 plus air cool
 Overage: 1250 °F ± 25 (677 °C ± 14), for 16 hours minimum plus air cool

This followed by a three part heat treatment.
Solution Treatment: 1625°F +/-25°F (885°C +/-14°C) for 1 hour, followed by a controlled quench.
Cold Stabilization: Cool to –100 °F ± 15 (-73 °C ± 8) for 1 hour minimum, air warm
 Ageing (standard): 900°F +/-10°F (482°C +/-6°C) for 5 hours, air cool

Typical Mechanical Properties

Availability
 AerMet® 100 is available in Bar (Rounds), Hollow Bar, Sheet, Plate, Weld Wire, Billet, Wire. For all stock availability contact Sales.

Specifications
UNS K92580
AMS 6532 - Bar and Forgings
AMS 6478
MIL STD 2154 CL A
MIL STD 2154 TYPE 1 CL A
MIL HDBK 5
MMS 217 EXC SONIC
 Aermet® 100 is a registered tradename of Carpenter Technologies

ales for further availability.

Specifications
Permalloy
HYMU 80
MAG 7904
MIL N 14411 C, COMP. 1
 ASTM A753-78 and ASTM 596